Organic polyisocyanate-alkylene oxide adhesive composition for preparing lignocellulosic composite products

ABSTRACT

An improved adhesive binder composition is provided for the preparation of lignocellulosic composite molded articles, especially flake or particleboard, made from moldable compositions which comprises an organic polyisocyanate-alkylene oxide or halogenated alkylene oxide and optionally lignin, for application to the lignocellulosic material prior to the molding process to form the composite product.

FIELD OF THE INVENTION

The present invention relates generally to the compression molding of lignocellulosic materials into composite bodies, sheets and the like and more particularly to an improved organic di- or polyisocyanate binder system for the lignocellulosic material which imparts equivalent or improved properties to the molded pressed composite product at substantially reduced isocyanate binder levels.

BACKGROUND OF THE INVENTION

The molding of lignocellulosic and lignocellulosic-containing fibers, particles or layers to form composite articles is known. The binders which normally are used are the synthetic resin glues such as a solution of urea-formaldehyde or phenol-formaldehyde resin in water. Composite products containing lignocellulose produced in this way lack durability and are susceptible to moisture conditions and deterioration in certain building purposes to which they may be subjected.

Di- and polyisocyanates as binders for lignocellulose materials have been proposed and are known to give products of increased stability and mechanical strength. Process technical advantages of polyisocyanates have been disclosed in German Offenlegungsschrift No. 2,109,686. Two problems associated with the use of polyisocyanate binders are (1) even at reduced binder use levels, the cost of the polyisocyanates as compared to the urea-formaldehyde or phenol-formaldehyde resin binders is unfavorable and (2) the viscosity of the normally employed polyisocyanate binders are much higher than the synthetic glue resins and are therefore difficult to apply to the lignocellulose with current application equipment or methods. The advent of technology to emulsify the polyisocyanates in water provided a binder product with reduced viscosity but with a service life of only 2 to 4 hours.

The present invention which comprises an improved polyisocyanate based adhesive binder composition that has been extended through the addition of alkylene oxides or halogenated alkylene oxides and optionally lignin, avoids the above mentioned disadvantages.

SUMMARY OF THE INVENTION

This invention relates to the preparation of a polyisocyanate-alkylene oxide or halogenated alkylene oxide binder composition and its use for the preparation of lignocellulosic composite molded products.

It is the principal object of this invention to provide an improved lignocellulosic binder and composition which gives properties equivalent to or better than prior molded pressed composite products at dramatically reduced di- or poly-isocyanate (referred to generally as polyisocyanates) levels and cost.

The advantages of the present invention is that reduced levels of the di- or poly-isocyanate necessary to produce a cured pressed composite lignocellulosic product can be substantially reduced while maintaining equivalent or superior composite board physical properties. By employing the di- or polyisocyanate-alkylene oxide or halogenated oxide combination, with or without the use of lignin as a diluent, the binder resin economics are equivalent or better than the synthetic glue resin economics. The composite products made with the adhesive binders of the present invention have superior physical properties to those prepared with the urea-formaldehyde or phenol-formaldehyde binder systems. The addition of the alkylene or halogenated alkylene oxides to the di- or polyisocyanates substantially reduces the overall viscosity of the binder system while exhibiting a marked increase in service life of greater than seven (7) days. The binder system of the present invention has viscosities equivalent to or lower than the formaldehyde type resin systems in water, which allows the instant binder system to be applied to the lignocellulosic chips, particles, etc., using present application technology. As a further advantage, the binder system of the present invention can be employed with high molecular weight or solid di- or polyisocyanates which by themselves would have properties which would preclude their use as adhesives for lignocellulosic products with current application techniques.

DESCRIPTION OF THE INVENTION

In accordance with the present invention an adhesive binder composition comprising an alkylene oxide or halogenated alkylene oxide having from 3 to 12 carbon atoms and an organic di- or polyisocyanate, with or without the addition of lignin, is provided for the preparation of lignocellulosic composite bodies or sheets which comprises shaping in a mold or between mold surfaces in the form of a caul plate or platen a mixture of the lignocellulosic material and the isocyanate based binder of the present invention generally at temperatures of from about 140° C. to 220° C., preferably 160° C. to 190° C., at pressures of from about 100 to 600 psi for a period of from 1 to 10 preferably 3 to 5 minutes, there being provided at the interface of the mixture and mold surface or surfaces a release agent such as a metallic soap.

The organic polyisocyanates are generally applicable as binders in the present invention. Organic polyisocyanates which may be used include aliphatic alicyclic and aromatic polyisocyanates characterized by containing two or more isocyanate groups. Such polyisocyanates include the diisocyanates and higher functionality isocyanates, particularly the aromatic polyisocyanates. Mixtures of polyisocyanates may be used which for example are the crude mixtures of di- and higher functionality polyisocyanates produced by phosgenation of aniline-formaldehyde condensates or as prepared by the thermal decomposition of the corresponding carbamates dissolved in a suitable solvent as described in U.S. Pat. Nos. 3,962,302 and 3,919,279 both known as crude MDI or PMDI. The organic polyisocyanate may be isocyanate-ended prepolymers made by reacting under standard known conditions, an excess of a polyisocyanate with a polyol which on a polyisocyanate to polyol basis may range from about 20:1 to 2:1 and include for example polyethylene glycol, polypropylene glycol, diethylene glycol monobutyl ether, ethylene glycol monoethyl ether, triethylene glycol, etc. as well as glycols or polyglycols partially esterfied with carboxylic acids including polyester polyols and polyether polyols. The organic polyisocyanates or isocyanate terminated prepolymer may also be used in the form of an aqueous emulsion by mixing such materials with water in the presence of an emulsifying agent. The isocyanates may also contain impurities or additives such as carbodiimides, isocyanurate groups, urea, hydrolyzable chlorides and biurets as well as certain release agents. Illustrative of such di- or polyisocyanates which may be employed include, for example, toluene-2,4- and 2,6-diisocyanates or mixtures thereof, diphenylmethane-4,4'-diisocyanate (a solid) and diphenylmethane-2,4'-diisocyanate (a solid) or mixtures of same, i.e., containing about 10 parts by weight 2,4'- or higher, which are liquid at room temperature, polymethylene polyphenyl isocyanates, naphthalene-1,5-diisocyanate, 3,3'-dimethyl diphenylmethane-4,4'-diisocyanate, triphenylmethane triisocyanate, hexamethylene diisocyanate, 3,3'-ditolylene-4,4-diisocyanate, butylene 1,4-diisocyanate, octylene-1,8-diisocyanate, 4-chloro-1,3-phenylene diisocyanate, 1,4- 1,3-, and 1,2-cyclohexylene diisocyanates and in general the polyisocyanates disclosed in U.S. Pat. No. 3,577,358. The preferred polyisocyanates are the diphenylmethane diisocyanate 2,4' and 4,4' isomers including the 2,2' isomer and the higher functional polyisocyanate and polymethylene polyphenyl isocyanate mixtures, which may contain from about 20 to 85 weight percent of the diphenylmethane diisocyanate isomers. Typical of the preferred polyisocyanates are those sold commercially as "Rubinate-M" (Rubicon Chemicals Inc.) and "Papi" (The Upjohn Co.). In general the organic polyisocyanates will have a molecular weight in the range between about 100 and 10,000 and will be employed in amounts of from about 20 to 95 parts by weight, preferably 40 to 60 parts by weight based on the polyisocyanate-oxide mixture.

The alkylene oxides and halogenated alkylene oxides employed in the present invention in amounts of from about 5 to 80 preferably 60 to 40 parts by weight based on the isocyanate-oxide binder mixture contain from 3 to 12 carbon atoms and include, for example propylene, butylene, amylene, heptylene, octylene, decene, dodecene oxides, etc. as well as the corresponding halogenated alkylene oxides such as 2-chloropropylene oxide (epichlorohydrin), trichlorooctylene oxide, 2-bromopropylene oxide, trichloro-, tribromo-, triiodobutylene oxides, 2-bromopropylene oxide, 2-chlorododecene oxide, etc.

As indicated hereinabove the addition of the alkylene or halogenated alkylene oxides substantially reduces the overall viscosity of the binder system providing ease of application. Typical of the viscosities attained in centipoise, (c.p.) at 25° C. are as follows using a diphenylmethane diisocyanate-polymethylene polyphenyl isocyanate mixture, sold commercially as "Rubinate-M" by Rubicon Chemicals Inc. and having a viscosity of 230 c.p. at 25° C. The viscosities were run for 30 minutes, 60 minutes and 4 hours, respectively at various ratios by weight of polyisocyanate to oxide.

    ______________________________________                                                     Propyl-                                                            230 c.p.    lene      Centipoise After                                         Isocyanate  Oxide     30 min.   60 min.                                                                              4 hr.                                    ______________________________________                                         3.0         0.5       17.6      17.9  19.2                                     2.5         1.0       5.1       5.1   5.8                                      2.0         1.5       1.6       1.9   1.9                                      1.5         2.0       1.0       1.0   1.0                                                  Epichloro-                                                                     hydrin                                                             3.0         0.5       42.9      42.9  43.5                                     2.5         1.0       14.7      14.7  15.6                                     2.0         1.5       6.7       6.7   6.7                                      1.5         2.0       3.7       3.7   3.7                                                  Butylene                                                                       Oxide                                                              3.0         0.5       21.4      22.4  23.5                                     2.5         1.0       6.1       6.4   6.4                                      2.0         1.5       1.9       1.9   1.9                                      1.5         2.0       1.3       1.3   1.3                                      ______________________________________                                    

In addition a solid diphenylmethane-4,4'-diisocyanate was mixed with propylene oxide at a parts by weight ratio of the 4,4' isomer to propylene oxide of 2.5:1.0, 2.0:1.5 and 3.0:0.5 and gave a cloudy liquid mixture with less than 50 c.p., a clear liquid mixture of 10 c.p. and liquid containing solids respectively.

The lignin which may be employed as a diluent in the binder system of the present invention are used in amounts of from 0 to 60 weight percent, preferably from 20 to 35 weight percent based on the total polyisocyanate-oxide-lignin mixture. The exact composition of lignin varies. Lignin derived from a variety of sources may be used in the binder system of the present invention to form the adhesive mixture. One source is a mixture of waste liquors resulting from the chemical pulping of ligno-cellulose. Suitable lignin which may be employed include, for example, purified pine wood lignin, kraft waste liquor, soda waste liquor, calcium, magnesium, sodium and ammonium base sulfite liquors, chlorinated waste liquors, etc. Lignins from hardwood and softwood sources may be used as well as lignins from acid-precipitated and alkali-reconstituted kraft liquors. The abundant and available chlorinated waste liquors derived from paper mill bleach may be used. The waste liquors may be used in their original condition in the adhesive binder composition of the instant invention. The lignin may also have a wide range of pH and a solids content of from about 10 to 90 weight percent. When employed, the lignin is simply physically mixed with the isocyanate-oxide adhesive when prepared or applied directly to the lignocellulosic material.

Lignocellulose, according to the present invention, used to prepare the lignocellulosic-containing composite articles include wood chips, wood fibers, shavings, sawdust, wood wool, cork, bark and the like products from the wood-working industry. Fibers, particles, etc. from other natural products which are lignocellulosic such as straw, flax residues, dried weeds and grasses, nut shells, hulls from cereal crops such as rice and oats and the like may be used. In addition, the lignocellulosic materials may be mixed with inorganic flakes or fibrous material such as glass fibers or wool, mica and asbestos as well as with rubber and plastic materials in particulate form. The lignocellulose may contain a moisture (water) content of up to about 25 percent by weight but preferably contains between 4 and 12 percent by weight.

In manufacturing lignocellulosic composite products for the purpose of this invention, such as flakeboard for example, a small amount of the binder (with or without lignin) along with the lignocellulosic material is simply milled or mixed uniformly together. Generally the isocyanate-oxide binding agent (with or without lignin) is sprayed onto the material while it is being mixed or agitated in suitable and conventional equipment. Various type mixing equipment such as an intensive-shear mixer may be employed. The binder use levels according to the present invention, based on the weight of oven dried (0% moisture content) lignocellulosic material is from about 1.5 to 12 preferably 2.5 to 6.5 weight percent. The lignocellulose-adhesive binder mixture is generally sprinkled or formed in the desired proportions onto a caul plate of aluminum or steel which serves to carry the "cake" into the press to give the desired thickness of product, the plates having been sprayed or coated with a release agent such as the metal soaps like the iron, calcium or zinc stearate compounds. Other conventional release agents such as sodium phenolate and certain tertiary amines may also be employed.

The following examples are provided to illustrate the invention in accordance with the principles of this invention but are not to be construed as limiting the invention in any way except as indicated by the appended claims.

In the Examples which follow, the test results set forth are expressed as ASTM D 1037 values and wherein

    ______________________________________                                         M.C.        is Moisture Content (%)                                            I.B.        is Internal Bond (psi)                                             T.S.        is cold water (25° C.) thickness swell,                                 24 hr. immersion (%)                                               PMDI        is a mixture of liquid diphenylmethane                                         diisocyanate-polymethylene polyphenyl                                          isocyanate having a 46.5% diphenyl-                                            methane diisocyanate content                                       P.O.        is propylene oxide                                                 B.O.        is butylene oxide                                                  C.P.O.      is 2-chloropropylene oxide                                         C.B.O.      is trichlorobutylene oxide                                         T.B.O.      is tribromobutylene oxide                                          H.O.        is heptylene oxide                                                 C.D.O.      is chlorodecene oxide                                              D.D.O.      is dodecene oxide                                                  TDI         is toluene-2,4-diisocyanate                                        TPMI        is triphenylmethane triisocyanate                                  CDI         is cyclohexylene-1,3-diisocyanate                                  ______________________________________                                    

EXAMPLE 1

580 g. of pine wood chips dried to a moisture content of 6 percent are placed in an open tumbler-mixer. During tumbling, 3.5 parts based on weight of the wood of an isocyanate based binding agent prepared by mixing 70 parts crude liquid diphenylmethane diisocyanate-polymethylene polyphenyl isocyanate (PMDI) mixture having 46.5 percent diphenylmethane diisocyanate content and 30 parts propylene oxide are sprayed over the chips by an air pressurized system. Two caul plates 12 inches square are sprayed evenly with a zinc stearate external release agent. Using a former box, a 10.5 inches square "cake" of the chip-binder mixture is formed on the caul plate. The second caul plate is placed over the cake which is pressed to stops at a thickness of 13 mm at 190° C. for 41/2 minutes after which the pressed cake is released from between the press plates and cut into specimens for physical testing. Test results of the composite board is 132 psi I.B. and a T.S. of 22 percent.

EXAMPLE 2 to 5

The procedure of Example 1 is repeated except that different levels of oxide are substituted with crude liquid diphenylmethane diisocyanate-polymethylene polyphenyl isocyanate (PMDI) mixture having 46.5 percent diphenylmethane diisocyanate content while maintaining the total binder level constant at 3.5 percent based on the weight of the wood.

                  TABLE 1                                                          ______________________________________                                         Ex.       PMDI    P.O.       I.B. T.S.                                         No.       (%)     (%)        (psi)                                                                               (%)                                          ______________________________________                                         2         85      15         173  18                                           3         78      22         141  21                                           4         43      57         114  25                                           5         100     0          161  17                                           ______________________________________                                    

EXAMPLES 6 to 9

The procedure of Examples 1 to 5 is repeated except with the following changes. The total binder level is held constant at 4.5 percent based on the weight of the wood. A third component, lignin, a product resulting from the chemical pulping of lignocellulose, is added to the binder mixture. The liquid diphenylmethane diisocyanate-polymethylene polyphenyl isocyanate (PMDI) mixture having a 46.5 percent diphenylmethane diisocyanate content and oxide content varies over the range specified in Table 2 below.

                  TABLE 2                                                          ______________________________________                                         Ex.    PMDI       Lignin  P.O.   I.B. T.S.                                     No.    (%)        (%)     (%)    (psi)                                                                               (%)                                      ______________________________________                                         6      66.8       22.2    11.0   149  23                                       7      61.0       22.2    16.8   165  22                                       8      55.5       22.2    22.3   142  19                                       9      44.4       22.2    33.4   143  24                                       ______________________________________                                    

EXAMPLES 10 to 15

The procedure of Examples 1 to 9 is repeated with the following changes. The crude liquid diphenylmethane diisocyanate-polymethylene polyphenyl isocyanate (PMDI) mixture having a 46.5 percent diphenylmethane diisocyanate content and lignin are varied over the ranges specified in Table 3 below while the oxide content is varied from 0 to 25 percent of the total binder which is based on weight of the wood.

                  TABLE 3                                                          ______________________________________                                                                      Total                                             Ex.  PMDI    Lignin     P.O. Binder  I.B. T.S.                                 No.  (%)     (%)        (%)  (%)     (psi)                                                                               (%)                                  ______________________________________                                         10   66.8    11.0       22.2 4.5     170  20                                   11   61.0    16.8       22.2 4.5     155  22                                   12   44.4    33.4       22.2 4.5     149  23                                   13   37.5    37.5       25.0 4.0     110  28                                   14   100.0   --         --   4.5     218  18                                   15   72.0    28.0       --   3.5     128  28                                   ______________________________________                                    

EXAMPLES 16 to 20

The procedure for Examples 1 to 15 are repeated except for the following changes: butylene oxide is substituted for propylene oxide. The binder level for 16 to 19 is held constant at 3.5 percent based on the weight of the wood. Example 20 includes 22 weight percent lignin with a 4.5 weight percent binder level. The liquid diphenylmethane diisocyanate-polymethylene polyphenyl isocyanate (PMDI) mixture having 46.5 percent diphenylmethane diisocyanate content and oxide percentages are varied according to Table 4 below.

                  TABLE 4                                                          ______________________________________                                         Ex.       PDMI    B.O.        I.B. T.S.                                        No.       (%)     (%)         (psi)                                                                               (%)                                         ______________________________________                                         16        100.0   --          147  25                                          17        78.5    21.5        150  25                                          18        71.0    29.0        135  27                                          19        57.0    43.0        111  29                                          20        55.0    22.3        115  28                                          ______________________________________                                    

EXAMPLE 21 (Comparative)

The procedure for Examples 1 to 20 are repeated except phenol formaldehyde resin (6 percent) is used as the binder and the pressing time is 9 minutes and pressing temperature 220° C. The following are the test results which indicates that a wax must be added to the material pressed to give desired properties.

    ______________________________________                                                 I.B. T.S.                                                                      (psi)                                                                               (%)                                                               ______________________________________                                                 101  32.3                                                              ______________________________________                                    

EXAMPLES 22 to 32

A number of runs are made in accordance with the procedure of Examples 1 to 5, utilizing various alkylene or halogenated alkylene oxides and polyisocyanate compositions. The binder level is maintained at 3.5 weight percent based on the weight of the wood. The oxides and isocyanates with test results are set forth in Table 5.

                  TABLE 5                                                          ______________________________________                                                            Poly-                                                       Ex.      Alkylene  Isocyanate  I.B. T.S.                                       No.      Oxide     (%)         (psi)                                                                               (%)                                        ______________________________________                                         22       C.P.O.    PMDI        138  20                                         23       C.B.O.    PMDI        125  24                                         24       T.B.O.    PMDI        120  25                                         25       H.O.      PMDI        130  21                                         26       C.D.O.    PMDI        125  23                                         27       D.D.O.    PMDI        125  24                                         28       P.O.      TDI         110  30                                         29       B.O.      TPMI        132  21                                         30       C.P.O.    TDI         105  31                                         31       P.O.      CDI         105  29                                         32       C.B.O.    CDI         100  30                                         ______________________________________                                     

We claim:
 1. An adhesive binder composition for the preparation of compression moldable lignocellulosic articles which comprises an organic di- or polyisocyanate, an alkylene oxide or halogenated alkylene oxide having from 3 to 12 carbon atoms and from 20 to 35 weight percent lignin added as diluent.
 2. The adhesive composition of claim 1 wherein the alkylene oxide or halogenated alkylene oxide is selected from the group consisting of propylene oxide, butylene oxide, 2-chloropropylene oxide, trichlorobutylene oxide, tribromobutylene oxide, heptylene oxide, chlorodecene oxide and dodecene oxide.
 3. The adhesive composition of claim 2 wherein the alkylene oxide is propylene oxide.
 4. The adhesive composition of claim 2 wherein the alkylene oxide is butylene oxide.
 5. The adhesive composition of claim 2 wherein the halogenated-alkylene oxide is 2-chloropropylene oxide.
 6. The adhesive composition of claim 1 wherein the di- or polyisocyanate is a diphenylmethane diisocyanate.
 7. The adhesive composition of claim 1 wherein the di- or polyisocyanate is a mixture of diphenylmethane diisocyanate and the higher functionality polymethylene polyphenyl isocyanates.
 8. The adhesive composition of claim 1 wherein from 40 to 60 weight percent organic di- or polyisocyanate and from 60 to 40 weight percent alkylene oxide or halogenated alkylene oxide is employed.
 9. A compression moldable lignocellulosic composition comprising lignocellulosic particles and from about 1.5 to 12 percent by weight based on oven dried particles of an adhesive binder composition which comprises from about 20 to 95 weight percent organic di- or polyisocyanate and from about 5 to 80 weight percent alkylene oxide or halogenated alkylene oxide having from 3 to 12 carbon atoms.
 10. The compression moldable composition of claim 9 wherein from 2.5 to 6.5 weight percent adhesive binder is employed in the composition.
 11. The compression moldable composition of claim 9 wherein from 0 to 60 weight percent lignin based on the total adhesive binder composition is added as diluent.
 12. The compression moldable composition of claim 11 wherein the lignin is between 20 and 35 weight percent.
 13. The compression moldable composition of claim 9 wherein the alkylene oxide or halogenated alkylene oxide is selected from the group consisting of propylene oxide, butylene oxide, 2-chloropropylene oxide, trichlorobutylene oxide, tribromobutylene oxide, heptylene oxide, chlorodecene oxide and dodecene oxide.
 14. The compression moldable composition of claim 13 wherein the alkylene oxide is propylene oxide.
 15. The compression moldable composition of claim 13 wherein the alkylene oxide is butylene oxide.
 16. The compression moldable composition of claim 13 wherein the halogenated alkylene oxide is 2-chloropropylene oxide.
 17. The compression moldable composition of claim 9 wherein from 40 to 60 weight percent organic di- or polyisocyanate and from 60 to 40 weight percent alkylene oxide or halogenated alkylene oxide is employed in the adhesive binder.
 18. The compression moldable composition of claim 9 wherein the di- or polyisocyanate is a diphenylmethane diisocyanate.
 19. The compression moldable composition of claim 9 wherein the di- or polyisocyanate is a mixture of diphenylmethane diisocyanate and the higher functionality polymethylene polyphenyl isocyanates.
 20. A composition board product comprising a compression molded lignocellulosic composition comprising lignocellulosic particles and from about 1.5 to 12 weight percent based on oven dried lignocellulosic particles employed of an adhesive binder composition, said binder composition being a mixture of from about 20 to 95 weight percent organic di- or polyisocyanate and from 5 to 80 weight percent alkylene or halogenated alkylene oxide having from 3 to 12 carbon atoms.
 21. The composition board product of claim 20 wherein from 0 to 60 weight percent lignin based on the total adhesive binder composition is added as diluent.
 22. The board product of claim 20 wherein the compression molded lignocellulosic composition is wood particle board.
 23. A method for the preparation of lignocellulosic composite articles comprising the steps of(a) mixing together lignocellulosic particles and from about 1.5 to 12 weight percent based on oven dried lignocellulosic particles of an adhesive binder composition comprising from 20 to 95 weight percent organic di- and polyisocyanate and from about 5 to 80 weight percent alkylene or halogenated alkylene oxide having from 3 to 12 carbon atoms to form a moldable composition; (b) introducing said moldable composition onto a metal mold, caul plate or platen which has been sprayed or coated with a release agent; (c) compression shaping said composition at temperatures of between about 140° C. to 220° C. at pressures of from about 100 to 600 psi for a period of from about 1 to 10 minutes to form a composite article of desired shape and/or thickness; and (d) thereafter releasing said lignocellulosic composite article from said metal mold, caul plate or platen.
 24. A method according to claim 23 wherein 2.5 to 6.5 weight percent adhesive binder composition is employed and comprises from 40 to 60 weight percent organic di- or polyisocyanates and from 60 to 40 weight percent oxides, the release agent is a metallic soap, the compression temperature is between 160° C. to 190° C. and the time period is from 3 to 5 minutes.
 25. A method according to claim 23 wherein the binder composition is a mixture of diphenylmethane diisocyanate and the higher functionality polymethylene polyphenyl isocyanates and propylene oxide.
 26. A method according to claim 23 wherein the compression molded lignocellulosic composition is wood particle board. 